1.Product Introduction:
FU-2,made by Iron powder sintering process, can avoid seizing shaft due to the oil content in the bushing. Same as bronze power bushings, FU-2 bushing has good performance of anti- friction if it works under low load. The embedded solid lubricants inside the material structure can continuously provide low friction working surface to the bearing, therefore the bearing service life is considerably extended. Comparing with the traditional sintered parts, this material is better at the wearing resistance and high temperature resistance features.
2.Product Technical Data:
Base material：FeC0.5
Load capacity：45N/mm2
Friction Coef.μ：0.15~0.20
Temperature limit：-80~160℃
Material Code | Final density g/cm3 | Oil content% | Apparenthardness HB | Crushing strengt MPa | Final density g/cm3 |
FeC0.5 | >6.2~6.7 | ≥12 | 50~100 | >300 | >6.2~6.7 |
Product Feature andApplication
1. Self-lubricating,harder,higherstrength.
2.Generally,moreeconomicalthanbronze,
3.Recommendedforhighload applicationsatlowspeeds.
Usedinfarmequipment,off-roadequipment, winches,sheaves,conveyors,pulleys,etc.
Product details
MICROSECTION
| Solid Lubricants |
| Oil pove | |
| Fe alloy |
Material Specification
Alloy | Fe | C | Other |
FeC0.5 | remain | <0.5 | <3.0 |